SW-SS05F1K--Sil Sol - Premium 5% Sil-Phos Brazing Rod
Developed primarily for use on copper, but its use has extended to other nonferrous copper based alloys. Used extensively on refrigeration units, air conditioning apparatus, electrical conductors, copper and brass fittings and copper to brass equipment.
Features/Benefits
- Exposure to pressured steam can also result in accelerated corrosion.
- For copper-base alloys, such as brass or bronze, the joints should be fluxed.
- Should not be used on nickel-base and iron-base alloys, as the phosphorus reacts with the nickel or iron to form brittle compounds at the interface of the joints.
- Should not be used where the joints are exposed to sulfur compounds, especially in gases or oils at temperatures above normal room temperature.
- The self fluxing property of this filler metal is effective on copper only.
Appearance: | Gray |
Liquidus: | 1495°F (812°C) |
Recommended Brazing Temp.: | 1545-1595°F (840-868°C) |
Density (Lbs/in³): | 0.29 Lbs/In |
Shelf Life: | Lifetime |
Packaging: | 18.5x.09 dia plastic tube |
Rod Length: | 18 inches |
Weight: | 1 lb. |
Quantity per pack: | 28 ea |
Electrical Conductivity (%IACS): | 9.6 |
Electrical Resistivity (Microhm-cm): | 18.1 |
Solidus: | 1190°F (643°C) |
HVAC |
Refrigeration |
Appliance |
SDS | Product Sheets | Cross Reference Information |
SW-SS05F1K_sds_001.pdf |
SW-SS05F1K_prd_001.pdf |
no entry |
Manuals | Application Sheets | Software |
no entry | no entry | no entry |
Replacement Part:Stay Silv 5
Part Description:
Manufacturer :Harris Product Group
Replacement Part:Sil-Fos 5
Part Description:
Manufacturer :Lucas Milhaupt
No Accessories Available
No FAQs available